Verlies aan Polycyclische Aromatische Koolwaterstoffen (PAK) tijdens uitloogproeven
Rood GA Wilde PGM de Masereeuw P
Rood GA
Wilde PGM de
Masereeuw P
Citations
Altmetric:
Series / Report no.
Open Access
Type
Report
Language
nl
Date of publication
1995-01-31
Year of publication
Research Projects
Organizational Units
Journal Issue
Title
Verlies aan Polycyclische Aromatische
Koolwaterstoffen (PAK) tijdens uitloogproeven
Translated Title
Losses of Polycyclic Aromatic Hydrocarbons (PAH)
during leaching tests
Published in
Abstract
In het kader van het project onderzoek verricht naar
uitloogproeven voor Polycyclische Aromatische Koolwaterstoffen (PAK). In
het onderhavige onderzoek wordt aandacht besteed aan het kwantificeren van
mogelijke verliezen als gevolg van vervluchtiging en adsorptie aan diverse
onderdelen van de testopstelling. Hierbij is gebruik gemaakt van een
analysemethode om PAK in eluaten te bepalen met behulp van resultaten zijn
maatregelen aanbevolen om verliezen tijdens de uitloogproef en de opwerking
van de eluaten te voorkomen.In het algemeen kan gesteld worden dat verlies
van PAK als gevolg van adsorptie voornamelijk optreedt voor de hoog
moleculaire PAK bij onderdelen die van kunststof (zoals teflon, polyamide)
vervaardigd zijn. Het gebruik van met name een polyamidefilter wordt ten
zeerste afgeraden. Glaswol blijkt een goed alternatief voor het
polyamidefilter te zijn. Daarnaast is het belangrijk om de lengte van de
teflon effluentslang van de kolom te minimaliseren. Het voorstel is om een
lengte van maximaal 0.5 meter voor te schrijven. Uit de resultaten blijkt
dat glazen vacuumfiltratie-opstelling met betrekking tot mogelijke verliezen
van PAK tijdens de filtratie meer geschikt is dan het hogedrukfiltratie
apparaat van teflon. Echter moet ook bij vacuumfiltratie rekening worden
gehouden met verliezen van de hogere PAK. Alleen verlies van naftaleen als
gevolg van vervluchtiging is aangetoond bij wateroplossingen die gedurende
10 dagen bij kamertemperatuur hebben gestaan. Voorgesteld wordt om de
kolomproef en de cascadeproef aan te passen: - vervang het teflon
ondersteuningsgaasje, polyamidefilter, glasvezelvoorfilter en 0.45 mum
geregenereerd cellulose filter door glaswol of een glasvezelvoorfilter ; -
filtratie van de eluaten door membraanfilter (doorsnee = 50 mm) door middel
van een glazen vacuumfiltratie-opstelling ; - De kolombuis dient te zijn
vervaardigd van glas en niet van teflon.
Research has been carried out on leaching tests for Polycyclic Aromatic Hydrocarbons (PAH) for the project study focuses on the quantitation of possible losses during the leaching tests due to volatilization and adsorption on parts of the equipment. Solid Phase Extraction (SPE) and quantitation of PAH with HPLC were used. Recommendations to prevent losses during the leaching test and treatment of the percolates are made on the basis of the results. In general, it was found that losses mainly of the higher PAHs took place due to adsorption on parts of the equipment, which were made of plastics like Teflon and polyamide. It is advised not to use the polyamide filter in particular. Glasswool proving to be a good alternative. It is also important to minimize the length of the Teflon tubing (max. 0.5 m). Losses of PAHs during vacuum filtration were found to be much lower than during the high-pressure filtration. However, vacuum filtration must take only losses of the higher PAHs into account. In a period of 10 days at room temperature only losses of naphthalene due to volatilization were detected. It is therefore proposed to modify the column test and batch test as follows: - replace the Teflon support gauze, the polyamide filter, glass prefilter and 0.45 mum regenerated cellulose membrane filter with glasswool or a prefilter of glass ; - filtrate the percolates through a membrane filter (cross section is 50 mm) by means of vacuum filtration-apparatus of glass ; - use a column made of glass and not Teflon.
Research has been carried out on leaching tests for Polycyclic Aromatic Hydrocarbons (PAH) for the project study focuses on the quantitation of possible losses during the leaching tests due to volatilization and adsorption on parts of the equipment. Solid Phase Extraction (SPE) and quantitation of PAH with HPLC were used. Recommendations to prevent losses during the leaching test and treatment of the percolates are made on the basis of the results. In general, it was found that losses mainly of the higher PAHs took place due to adsorption on parts of the equipment, which were made of plastics like Teflon and polyamide. It is advised not to use the polyamide filter in particular. Glasswool proving to be a good alternative. It is also important to minimize the length of the Teflon tubing (max. 0.5 m). Losses of PAHs during vacuum filtration were found to be much lower than during the high-pressure filtration. However, vacuum filtration must take only losses of the higher PAHs into account. In a period of 10 days at room temperature only losses of naphthalene due to volatilization were detected. It is therefore proposed to modify the column test and batch test as follows: - replace the Teflon support gauze, the polyamide filter, glass prefilter and 0.45 mum regenerated cellulose membrane filter with glasswool or a prefilter of glass ; - filtrate the percolates through a membrane filter (cross section is 50 mm) by means of vacuum filtration-apparatus of glass ; - use a column made of glass and not Teflon.